open porosity
开孔孔隙度
常用释义
英式发音
美式发音
基本释义
- 开孔孔隙度；开孔率
例句
-
1·The results show that the SSFs' bending strength gradually increases and the open porosity falls with increasing the slurry loading in precursor;研究发现：随前驱体中浆料浸入量的增加，泡沫制品的抗弯强度逐渐提高，开孔率有所降低；
-
2·Correlation coefficients between the thermal conductivity and bulk density, open porosity, permeability and raw material grade was obtained respectively.另外，还计算了导热系数与体积密度、显气孔率、透气度和原料等级之间的相关系数。
-
3·So that, it is necessary to adopt very sinterable UO2 powder and suitable pelleting and sintering conditions to minimize open porosity and small porosity.因此，必须采用烧结性良好的UO_2粉末和合适的成型烧结条件以使开口孔隙度和细孔隙度降至最低。
-
4·The foamed ceramic material with high open porosity is characterized by low apparent density , high permeability, and resistance to high temperature and chemical corrosion.泡沫陶瓷具有密度小、透气性高、耐高温、抗化学腐蚀等特性。
-
5·The use of U3O8 additive can improve the pellet microstructure, but result in decrease of pellet density and increase of open porosity, which contributes strongly to moisture.采用U_3O_8添加剂可改善芯块微观结构，但同时使芯块密度下降，开口孔隙度增加进而导致吸湿加剧。
-
6·The effects of sintering schedule on the shrinkage, open porosity and bending strength of the stainless steel foam with 3-D opened network structure were investigated in this paper.研究了烧结制度对具有三维通孔网状结构泡沫不锈钢的线收缩率、开孔孔隙度、抗弯强度的影响。
-
7·The compactness bending strength, compressive strength, shore-hardness of carbon slides impregnated with metals were increased; while open porosity and electrical resistivity decreased.炭滑板经浸渍金属后，致密性、抗折强度、抗压强度、肖氏硬度明显提高，而开口气孔和电阻率降低。
-
8·Based on the experiment results on three kinds of open graded ATPB, it is concluded that asphalt content should be above 2.5% and porosity should be above 18%.本文经对三种开级配的沥青稳定碎石进行了试验研究，得出ATPB的沥青用量应在2.5%以上，空隙率在18%以上的结论。
-
9·The porosity of porous Al-Si alloy is 40~80% and percentage of open-cell is above 85%, bom of which vary with the fabrication process of preform.孔隙率在40～80%，孔隙连通率在85%以上，孔隙的大小和孔隙率取决于预制块的制备工艺。