notched impact strength
缺口冲击强度：用于衡量材料在缺口处受到冲击时的抗断裂能力的指标。
常用释义
英式发音
美式发音
基本释义
- 缺口冲击强度：用于衡量材料在缺口处受到冲击时的抗断裂能力的指标。
例句
-
1·The results showed that the using amount of PC had a great effect on the notched impact strength.结果表明，对共混体系缺口冲击强度影响较大的为体系中PC的含量。
-
2·The results showed that with increasing content of TPU, elongation at break and notched impact strength of the blends increased.拉伸强度和断裂伸长率均随辛醛含量的增加而降低。
-
3·With increasing content of the fillers, the notched impact strength and the tensile strength of PVC-matrix composites improved simultaneously.随着复合粒子用量的增加，复合材料的强度和韧性同时提高，复合粒子高含量时，复合材料的拉伸强度稍有下降。
-
4·The results showed different blending methods had little effects on tensile strength of the blends, but obvious effects on notched impact strength and morphology.结果发现，共混方式对共混体系拉伸强度影响不大，但对冲击强度和断面形态影响较大。
-
5·The results showed that the impact strength(notched) of the composite was maximum and the mechanical and thermal properties were less decreased, when the dosage of modifier was 12 PHR.当复合冲击改性剂用量为12份时，材料的冲击强度达到最大值，其它力学和热性能降低不大。
-
6·The notched Izod impact strength of alloy increases with the increasing of EMG content in the condition of keeping other mechanical properties.而随着EM G含量的增加，材料的冲击强度显著提高，且其它的力学性能基本保持不变。
-
7·Many round voids which result in stress concentration easily are found on SEM micrographs of fracture surface after heat-treatment, so the notched izod impact strength of the sample decreases.由热处理后试样冲击断面的SEM照片可见水分挥发留下的空洞，这些空洞容易形成应力集中点，因而导致冲击韧性降低。
-
8·The result showed that the tensile strength property and Vicat softening temperature was increased and notched impact property of PVC/ABS composite was decreased with the glass fiber added.研究结果表明：随着玻璃纤维添加份数的增加，PVC/ABS合金的拉伸性能和维卡软化温度有不同程度的提高，缺口冲击强度有所下降。
-
9·The results show that the addition of mica can enhance the flexural strength, flexural modulus, notched Izod impact strength and heat deformation temperature of the composites;结果表明：云母可有效提高PP的弯曲强度及模量、悬臂梁缺口冲击强度和耐热性能；